Ethylene Methyl Acrylate Copolymer
/EMA
**************************************
Copyright 2002 by Roger D. Corneliussen
**************************************
To jump to a particular property, click on the name listed below.
From Modern Plastics Encyclopedia 99, p. B-198
Melt
Flow
Melting
Temperature
Glass
Transition
Processing Molding Pressure
Processing Molding Temperature
Compression
Ratio
Mold
Shrinkage
Tensile
Strength
Elongation
Tensile
Yield Strength
Compressive
Strength
Flexural
Strength
Tensile
Modulus
Flexural
Modulus
Izod
Impact Strength
Hardness
Deflection
Temperature
Thermal
Expansion
Thermal
Conductivity
Specific
Gravity
Dielectric
Strength
Water
Absorption
Note:
The ASTM numbers are linked to
their descriptions on the ASTM website.
To go to the description, simply
click on the ASTM number
Melt
Flow
ASTM D1238
(gm/10 min)
--- gm /10 min
Melting
Temperature degrees C
Tm Crystalline
83 C
Glass
Transition
(C)
Tg (Amorphous)
--- C
Processing
Temperature
Range Degrees F
Extrusion
200 to 620 F for extrusion
Molding
Pressure Range ( PSI) (ksi)
--- psi
--- ksi
--- MPa
To
go back to the top of this page, click on
Top
Mold(Linear)
Shrinkage (in/in)
ASTM D955
--- in/in
Tensile
Strength at Break
ASTM D638
1650 psi
11 MPa
To
go back to the top of this page, click on
Top
Elongation
at break (%)
ASTM D638
740 %
Tensile
Yield Strength (psi)
ASTM D638
1650 psi
11 MPa
Compressive
Strength (psi)
Rupture or Yield
ASTM
D695
--- psi
--- MPa
To go to Compressive Strength Values,
click on
Compressive Strength
To
go back to the top of this page, click on
Top
Flexural
Strength (psi)
Rupture or Yield
ASTM D790
--- psi
--- MPa
Tensile
Modulus (psi)
ASTM D638
12000 psi
0.08 GPa
To go to Modulus Values,
click on
Modulus
Compressive
Modulus (psi)
ASTM
D695
--- psi
--- GPa
To
go back to the top of this page, click on
Top
Flexural
Modulus (psi)
ASTM D790
At 73 F
--- psi
--- GPa
At 200 F
--- psi
--- GPa
At 250 F
--- psi
--- GPa
At 300 F
--- psi
--- GPa
Izod
Impact (ft-lb/in of notch)
ASTM D256
--- ft lb/in of notch
To go to Izod Values,
click on
Izod
To
go back to the top of this page, click on
Top
Hardness
Rockwell ASTM D785
---
--
Shore D65 ASTM
D2240/D2583
---
Coefficient
of Linear Thermal Expansion
(10 exp-6 )in/in/C
--- (10 x exp –6) in/in /C
--- in/in /C
Deflection
Temperature under flexural load (F)
ASTM D648
264 psi ---
--- F
66 psi ---
--- F
To
go back to the top of this page, click on
Top
Thermal
Conductivity
(10 x exp –4)al cm/sec cm2 C
ASTM C177
--- (10 x exp –4) cal cm/sec cm2
--- cal cm/sec cm2
Specific
Gravity
ASTM D792
0.942 to 0.945
To go to Density /Specific Gravity Values,
click on
Density
Water
Absorption
(1/8 in thick specimen) (%)
ASTM D570
24 hr ------ %
Saturation
--- %
Dielectric Strength v/mil
(1/8 in thick Specimen; short time)
--- v/mil
**************************************
Copyright 2002 by Roger D.
Corneliussen
No part of this transmission is to be
duplicated, in any manor, or forwarded by
electronic mail without the express written
permission of Roger D. Corneliussen
**************************************
4/12/2000: