Silicone
Casting resins (RTV)
**************************************
Copyright 2002 by Roger D. Corneliussen
**************************************
Values are from Modern Plastics Encyclopedia 99.
To jump to a particular property, click on the name below.
Melt
Flow
Melting
Temperature
Glass
Transition
Processing Molding Pressure
Processing Molding Temperature
Compression
Ratio
Mold
Shrinkage
Tensile
Strength
Elongation
Tensile
Yield Strength
Compressive
Strength
Flexural
Strength
Tensile
Modulus
Flexural
Modulus
Izod
Impact Strength
Hardness
Deflection
Temperature
Thermal
Expansion
Thermal
Conductivity
Specific
Gravity
Dielectric
Strength
Water
Absorption
Note:
The ASTM numbers are linked to
their descriptions on the ASTM website.
To go to the description, simply
click on the ASTM number
Melt
Flow
ASTM D1238
(gm/10 min)
--- gm /10 min
Melting
Temperature degrees C
Tm Crystalline
--- C
Glass
Transition
(C)
Tg (Amorphous)
--- C
Processing
Temperature
Range Degrees F
Extrusion
--- F for Compression Molding
--- F for Injection Molding
--- F for Extrusion
Molding
Pressure Range ( PSI) (ksi)
--- psi
--- ksi
--- MPa
To
go back to the top of this page, click on
Top
Mold(Linear)
Shrinkage (in/in)
ASTM D955
0.000 to 0.006 in/in
Tensile
Strength at Break
ASTM D638
350 to 1000 psi
2.3 to 6.7 MPa
To
go back to the top of this page, click on
Top
Elongation
at break (%)
ASTM D638
20 to 700 %
Tensile
Yield Strength (psi)
ASTM D638
--- psi
--- MPa
Compressive
Strength (psi)
Rupture or Yield
ASTM
D695
--- psi
--- MPa
To go to Compressive Strength Values,
click on
Compressive Strength
To
go back to the top of this page, click on
Top
Flexural
Strength (psi)
Rupture or Yield
ASTM D790
--- psi
--- MPa
Tensile
Modulus (psi)
ASTM D638
--- psi
--- GPa
To go to Modulus Values,
click on
Modulus
Compressive
Modulus (psi)
ASTM
D695
--- psi
--- GPa
To
go back to the top of this page, click on
Top
Flexural
Modulus (psi)
ASTM D790
At 73 F
--- psi
--- GPa
At 200 F
--- psi
--- GPa
At 250 F
--- psi
--- GPa
At 300 F
--- psi
--- GPa
Izod
Impact (ft-lb/in of notch)
ASTM D256A
--- ft lb/in of notch
To go to Izod Values,
click on
Izod
To
go back to the top of this page, click on
Top
Hardness
Rockwell ASTM D785
--
Shore D65 ASTM
D2240/D2583
A10 to 70
Coefficient
of Linear Thermal Expansion
(10 exp-6 )in/in/C
10
to 19 (10 x exp –6) in/in /C
0.000 010 to 0.000 019 in/in /C
Deflection
Temperature under flexural load (F)
ASTM D648
264 psi ---
--- F
66 psi ---
--- F
To
go back to the top of this page, click on
Top
Thermal
Conductivity
(10 x exp –4)al cm/sec cm2 C
ASTM C177
3.5 to 7.5 (10 x exp –4) cal cm/sec cm2
0.00035 to 0.00075 cal cm/sec cm2
Specific
Gravity
ASTM D792
0.97 to 2.5
To go to Density /Specific Gravity Values,
click on
Density
Water
Absorption
(1/8 in thick specimen) (%)
ASTM D570
24 hr --- 0.1 %
Saturation
--- %
Dielectric Strength v/mil
(1/8 in thick Specimen; short time)
400 to 550 v/mil
**************************************
**************************************
Copyright 2002 by Roger D.
Corneliussen
No part of this transmission is to be
duplicated, in any manor, or forwarded by
electronic mail without the express written
permission of Roger D. Corneliussen
**************************************